| THESE ARE 100% SOLID, HIGH STRENGTH, SPECIFIC METAL CONTENT MACHINABLE SYSTEM
FOR ECONOMICAL AND DEPENDABLE MAINTENANCE AND PERMANENT REPAIR WORKS. |
| |
| Salient Features |
 |
Versatile repair to metal and glass against corrosion. |
|
Can be machined like metal after curing. |
|
No twisting, bending, internal stresses as faced in welding. |
|
Very economical compared to tig welding of Titanium, Aluminium Etc. |
|
| |
| Typical Application |
|
Repair corroded areas like Impeller, Casing, Propeller Shafts, Key Ways, Tanks area. |
|
Repair specialized metal parts like Aluminium, Gunmetal, Titanium etc. |
|
Cooling System of Vacuum furnaces, Fractured Castings, Prototype parts/patterns, can be
repaired/prpared. |
|
Can be used to repair floating roof of tank and to fill gap between Heat Exchanger Tube sheet and Tube. |
|
| |
| Physical Properties |
| |
Poly Steel |
Poly SS/Alu./Bronze |
Titanium |
Nc Poly Metal |
| Compressive Strength : |
750 kg/cm" |
750 kg/cm2 |
700 kg/cm2 |
850 kg/cm2 |
| Flexural Strength : |
500 kg/cm2 |
500 kg/cm2 |
550 kg/cm2 |
450 kg/cm2 |
| Working Time @30oc : |
20-30 Min |
20-30 Min |
20-30 Min. |
20-30 Min |
| Curing Time : |
3 Hours |
3 to 4 Hours |
3 Hours |
3 to 4 Hours |
| Coverage Area : |
2.5 kg/sqm. |
1.8-2.5 kg/sqm. |
2.0-2.2 kg/sqm |
2.0-2.2 kg/sqm |
|
| |
|
|
|